orthogonal turning

During orthogonal turning by using a single point cutting tool, feed rate is 0.24 mm/rev. The uncut chip thickness is 0.23 mm. The shear angle, tangential force component, and radi...

In orthogonal turning of a cylindrical tube of wall thickness 5 mm, the axial and the tangential cutting forces were measured as 1259 N and 1601 N, respectively. The measured chip...

Following data correspond to an orthogonal turning of a 100 mm diameter rod on a lathe. Rake angle: +15°; Uncut chip thickness: 0.5 mm; nominal chip thickness after the cut: 1.25 m...

Orthogonal turning of a mild steel tube with a tool of rake angle $${10^0}$$ is carried out at a feed of $$0.14$$ $$mm/rev.$$ If the thickness of the chip produced is $$0.28mm,$$ t...

An orthogonal turning operation is carried out under the following conditions; rake angle $$ = {5^ \circ },$$ spindle rotational speed $$=400$$ $$rpm,$$ axial feed $$=0.4$$ $$m/min...

During pure orthogonal turning operation of a hollow cylindrical pipe, it is found that the thickness of the chip produced is $$0.5mm.$$ The feed given to the zero degree rake angl...

In orthogonal turning of a bar of $$100$$ $$mm$$ diameter with a feed of $$0.25$$ $$min/rev,$$ depth of cut of $$4$$ $$mm$$ and cutting velocity of $$90$$ $$m/min,$$ it is observed...

In orthogonal turning of a bar of $$100$$ $$mm$$ diameter with a feed of $$0.25$$ $$min/rev,$$ depth of cut of $$4$$ $$mm$$ and cutting velocity of $$90$$ $$m/min,$$ it is observed...

Orthogonal turning is performed on a cylindrical work piece with shear strength of $$250Mpa.$$ The following conditions are used: cutting velocity is $$180m/min,$$ feed is $$0.2mm/...

In orthogonal turning of medium carbon steel, the specific machining energy is $$2$$ $$kJ/m{m^3},$$ the cutting velocity, feed and depth of cut are $$120m/min,$$ $$0.2mm/rev$$ and...

In orthogonal turning of a low carbon steel bar of diameter $$150mm$$ with uncoated carbide tool, the cutting velocity is $$90m/min,$$ The feed is $$0.24mm/rev$$ and the depth of c...

During orthogonal turning of a steel rod by zero rake tool at feed $$0.25mm/rev$$ and depth of cut $$2.0mm,$$ the following observations were obtained. Tangential component of cutt...